【摘要】 研究了热挤压态MB26镁合金的静态与动态再结晶过程。结果表明该合金静态再结晶很难完成，而动态再结晶却能在短时间内获得等轴细晶组织。其再结晶粒尺寸比静态再结晶的均匀细小。再结晶为该合金的超塑变形提供了组织条件。
关键词：MB26合金 静态再结晶 动态再结晶
Proe网 ugproe.com
Static and Dynamic Recrystallization of MB26 Alloy
Ma Hongtao①，Yang Yunlin②，Zhang Baiqing①，Fang Hongsheng①
（①Department of Materials，Tsinghua University，Beijing 100084）
（②Luoyang Institute of Technology） 中国模具视频网
【Abstract】 The microstructure of MB26 alloy during static and dynamic recrystallization process was studied．The results shown that the recrystalliztion was difficult to be fully completed in static recrystallization，but it could be completed easily in dynamic process，and the grain size acquired by dynamic recrystallization was smaller than that of static recrystallization．The recrystallization provided a proper microstructure for the superplastic deformation of MB26 alloy．
Key words：MB26 alloy，static recrystallization，dynamic recrystallization
模具网 ugproe.com
1 前言
MB26合金是北京航空材料研究所在MB15（相当美国ZK60A）合金基础上添加富钇混合稀土元素研制成功的新型高强度镁合金［1］。文献［2～4］研究表明，该合金不仅比MB15合金有更好的室温及高温力学性能，而且具有更好的超塑变形能力。为研究该合金超塑变形机制，本文对热挤态的MB26合金静态再结晶和动态再结晶过程进行了观察与分析，获得一些有益的结论。
2 试验材料和方法
MB26合金主要化学成分w（％）为：5.4～5.79Zn、0.48～0.66Zr、1.0～1.65RE，余量为镁。铸态组织由α相和晶间网状第二相构成［1］。铸锭经350℃保温2h后先挤压成φ25mm的棒材，在同样条件下二次挤压成φ14mm的棒料，显微组织呈纤维状见图1。 UG网，首选ugproe.com
Proe网 ugproe.com
图1 MB26合金试样纵剖面原始组织 ×500 中国模具视频网
再结晶退火在箱式电阻炉中进行，动态再结晶试验在经改装的WJ-10A型机械式万能试验机上进行，加热炉为3kW管式电阻炉，均温区内温差±2℃。
利用Olympas金相显微镜对变形过程中的显微组织进行分析。晶粒尺寸和再结晶体积分数采用截线法测量。
3 试验结果与分析
3.1 静态再结晶
模具网 ugproe.com
图2 MB26合金经二次挤压后再结晶退火组织 ×500
400℃×50min UG网，首选ugproe.com
UG网，首选ugproe.com
图3 MB26合金再结晶体积分数、晶粒
尺寸随时间变化曲线 （400℃）
Proe网 ugproe.com
模具网 ugproe.com
UG网，首选ugproe.com
图4 MB26合金变形后试样的组织对比（400℃） 中国模具视频网
（a）夹头处的组织 δ＝0 ×500
（b）变形部分组织 δ＝200％ ×500
中国模具视频网